Simultaneous removel of h2s and so2 from tail gases

ABSTRACT

A process for the simultaneous removal of H 2 S and SO 2  from tail gases is disclosed. A tail gas stream is contacted with a sorbent in a sorption zone to produce a product gas stream and a sulfur laden sorbent, wherein the sorbent comprises Zn and a promoter metal.

FIELD OF THE INVENTION

The present invention relates generally to contaminant removal from tailgas streams. In another aspect, the present invention relates to aprocess for removing one or more contaminants from a tail gas stream viacontact with a regenerable sorbent.

BACKGROUND OF THE INVENTION

Tail gas streams originate from various sources. They are found inrefinery off-gases as well as Claus units that are unable to convert allgaseous sulfur species to elemental sulfur. These tail gases contain SO₂and H₂S at levels exceeding permissible emission limits which arecurrently set at 10 ppm H₂S and 250 ppm SO₂ in the United States. Tailgas compositions vary widely depending on the application. Often steam,syngas, and/or CO₂ are found in tail gases. Tail gases are mostly freeof O₂ but often contain low levels of H₂.

One way to treat tail gases is by hydrotreating and amine scrubbing.Hydrotreating requires the whole gas stream to be heated to reactiontemperature following a gas cool-down from 400° C. to near ambienttemperatures prior to use. Inherent in this process is a significantenergy penalty due to the heating and cooling steps required. The amineregeneration produces concentrated H₂S which is returned to a Claus unitwhere it is converted to elemental sulfur.

Alternatively, the gas can be oxidized in a burner to form SO₂ as theonly sulfur species. This option also requires a cool-down phase andadditional equipment to scrub the SO₂ and to regenerate the scrubbingmaterial. This is known as the CANSOLV® process (CANSOLV is a registeredtrademark of Cansolv Technologies, Inc.) and the regeneration producesconcentrated SO₂ which is recycled to a Claus unit.

Accordingly, a need exists for a process to remove contaminants from atail gas stream that eliminates the heating-up and cooling-down stepsfrom the alternative processes.

SUMMARY OF THE INVENTION

In one embodiment of the present invention, there is provided a processfor the simultaneous removal of SO₂ and H₂S, the process comprising,consisting of or consisting essentially of: a) contacting a tail gasstream comprising, consisting of, or consisting essentially of SO₂ andH₂S with a sorbent in a sorption zone to produce a product gas streamand a sulfur laden sorbent, wherein the sorbent comprises Zn and apromoter metal; and b) contacting at least a portion of the sulfur ladensorbent with a regeneration gas stream in a regeneration zone to producea regenerated sorbent and an off-gas stream.

In another embodiment of the present invention there is provided aprocess for the simultaneous removal of SO₂ and H₂S, the processcomprising, consisting of, or consisting essentially of: a) reducing asorbent with a reducing agent in a reduction zone to form a reducedsorbent, wherein the reduced sorbent comprises Zn, expanded perlite, anda promoter metal, wherein at least a portion of the reduced sorbentcomprises a substitutional solid solution characterized by the formulaM_(Z)Zn_((1-Z))Al₂O₄ and a substitutional solid metal solutioncharacterized by the formula M_(A)Zn_(B), wherein M is a promoter metalcomponent and A, B, and Z are in the range of from about 0.01 to about0.99; b) contacting the reduced sorbent with a tail gas streamcomprising SO₂ and H₂S in a sorption zone to produce a product gasstream and a sulfur laden sorbent; c) regenerating the sulfur ladensorbent in a regeneration zone to produce a regenerated sorbent and anoff gas comprising SO₂; d) returning at least a portion of theregenerated sorbent to said sorption zone; and e) recycling the SO₂containing off gas to a SO₂ treatment zone.

BRIEF DESCRIPTION OF THE FIGURES

FIG. 1 is a schematic diagram of a contaminant removal system inaccordance with one embodiment of the present invention.

FIGS. 2, 3, 4, 5, and 6 are plots of the time elapsed vs. ion currentfrom Mass Spectral Analysis of different components in tail gas duringruns in which simulated tail gas feeds are contacted with sorbents.

DETAILED DESCRIPTION OF THE INVENTION

Referring to FIG. 1, a contaminant removal system 10 is illustrated asgenerally comprising a tail gas source 12, a sorption zone 14, a productgas user 16, a drying zone 18, a regeneration zone 20, and an off-gasuser 22. In general, a tail gas stream exiting tail gas source 12 can becontacted with a sorbent in sorption zone 14 to thereby remove one ormore contaminants from the gas stream. The resulting,contaminant-depleted product gas stream exiting sorption zone 14 can berouted to product gas stream 16, while at least a portion of thecontaminant-laden sorbent can be dried in drying zone 18 prior to beingregenerated via contact with a regeneration gas in regeneration zone 20.The resulting off-gas stream exiting regeneration zone 20 can be routedto off-gas conduit 22, while at least a portion of the regeneratedsorbent can then be returned to sorption zone 14 via conduit 124 forsubsequent reuse. In one embodiment, at least one of the sorption,drying, and regeneration zones 14, 18, 20 can be contained within thesame process vessel. In another embodiment, at least one of thesorption, drying, and regeneration zones 14, 18, 20 can be contained intwo or more separate process vessels. Further, the contaminant removalsystem 10 depicted in FIG. 1 can be operated in continuous,semi-continuous, semi-batch, or batch mode. The operation of contaminantremoval system 10 will now be described in more detail below.

Tail gas source 12 can comprise any source or system capable ofproducing a gas stream. In one embodiment, the tail gas stream from gassource 12 can comprise in the range of from about 1 ppmv to about 30volume percent (1 vol. %=10,000 ppmv), from about 1 ppmv to about 10volume percent, from about 1 ppmv to about 1 volume percent, or from 1ppmv to 1000 ppmv of SO₂. In one embodiment, the tail gas stream fromgas source 12 can comprise in the range of from about 1 ppmv to about 60volume percent, from about 1 ppmv to about 20 volume percent, from about1 ppmv to about 5 volume percent, or from 1 ppmv to 5000 ppmv of H₂S.For example, gas source 12 can comprise a Claus unit, a refinery orchemical plant process stream, or any other suitable source.

In one embodiment, the ratio of H₂S to SO₂ in the tail gas streamexiting gas source 12 can be about 100:1, 10:1, 2:1, or 1:1. The tailgas stream can further comprise compounds selected from the groupconsisting of steam, syngas, CO₂, and combinations of any two or morethereof.

As depicted in FIG. 1, at least a portion of the tail gas stream exitinggas source 12 in conduit 112 can be routed into sorption zone 14,wherein the stream can be contacted with a sorbent to remove at least aportion of at least one contaminant from the incoming gas stream. In oneembodiment, the tail gas stream is not cooled prior to entering sorptionzone 14 and can have a temperature that is within about 200° C., about100° C., or 50° C. of the temperature of the tail gas stream exiting gassource 12. Generally, the tail gas stream entering sorption zone 14 canhave a temperature in the range of from about 150° C. to about 700° C.,about 250° C. to about 600° C., or 350° C. to 450° C. and in the rangeof from about atmospheric to about 750 psig, about 250 psig to about 600psig, or 350 psig to 450 psig.

In general, the sorbent employed in sorption zone 14 can be anysufficiently regenerable zinc-oxide-based sorbent composition havingsufficient contaminant removal ability. While described below in termsof its ability to remove sulfur contaminants from an incoming tail gasstream, it should be understood that the sorbent of the presentinvention can also have significant capacity to remove one or more othercontaminants. While not wishing to be bound by theory, it is believedthat nickel subsulfide (NiS₂) is formed by the reaction of nickelsulfide (NiS) and SO₂ in the presence of hydrogen. Nickel sulfide canoriginate from the reaction of nickel oxide and H₂S. The suspectedreaction mechanism is as follows:

NiO+H₂S NiS+H₂O+ΔH

NiS+SO₂+2H₂ NiS₂+2H₂O+ΔH

In one embodiment of the present invention, the sorbent employed insorption zone 14 can comprise zinc and a promoter metal component. Thepromoter metal component can comprise one or more promoter metalsselected from the group consisting of nickel, cobalt, iron, manganese,tungsten, silver, gold, copper, platinum, zinc, tine, ruthenium,molybdenum, antimony, vanadium, iridium, chromium, palladium, andmixtures thereof. In one embodiment, at least a portion of the promotermetal component is present in a reduced-valence state. The valencereduction of the promoter metal component can be achieved by contactingthe sorbent with a reducing agent within sorption zone 14 and/or priorto introduction into sorption zone 14. Any suitable reducing agent canbe used, including, but not limited to hydrogen and carbon monoxide.

In one embodiment of the present invention, the reduced-valence promotermetal component can comprise, consist of, or consist essentially of, asubstitutional solid metal solution characterized by the formula:M_(A)Zn_(B), wherein M is the promoter metal and A and B are eachnumerical values in the range of from about 0.01 to about 0.99. In theabove formula for the substitutional solid metal solution, A can be inthe range of from about 0.70 to about 0.98 or 0.85 to 0.95 and B can bein the range of from about 0.03 to about 0.30 or 0.05 to 0.15. In oneembodiment, A+B=1.

Substitutional solid solutions are a subset of alloys that are formed bythe direct substitution of the solute metal for the solvent metal atomsin the crystal structure. For example, it is believed that thesubstitutional solid metal solution M_(A)Zn_(B) is formed by the solutezinc metal atoms substituting for the solvent promoter metal atoms.Three basic criteria exist that favor the formation of substitutionalsolid metal solutions: (1) the atomic radii of the two elements arewithin 15 percent of each other; (2) the crystal structures of the twopure phases are the same; and (3) the electronegativities of the twocomponents are similar. The promoter metal (as the elemental metal ormetal oxide) and zinc (as the elemental metal or metal oxide) employedin the sorbent described herein typically meet at least two of the threecriteria set forth above. For example, when the promoter metal isnickel, the first and third criteria, are met, but the second is not.The nickel and zinc metal atomic radii are within 10 percent of eachother and the electronegativities are similar. However, nickel oxide(NiO) preferentially forms a cubic crystal structure, while zinc oxide(ZnO) prefers a hexagonal crystal structure. A nickel zinc solidsolution retains the cubic structure of the nickel oxide. Forcing thezinc oxide to reside in the cubic structure increases the energy of thephase, which limits the amount of zinc that can be dissolved in thenickel oxide structure. This stoichiometry control manifests itselfmicroscopically in an approximate 92:8 nickel zinc solid solution(Ni_(0.92)Zn_(0.08)) that is formed during reduction and microscopicallyin the repeated regenerability of sorbent.

In addition to zinc and the promoter metal, the sorbent employed insorption zone 14 can further comprise a porosity enhancer (PE) and analuminate. The aluminate can comprise a promoter metal-zinc aluminatesubstitutional solid solution characterized by the formula:M_(Z)Zn_((1-Z))Al₂O₄ wherein M is the promoter metal and Z is in therange of from 0.01 to 0.99. The porosity enhancer, when employed, can beany compound which ultimately increases the macroporosity of thesorbent. In one embodiment, the porosity enhancer can comprise perlite.Examples of sorbents suitable for use in sorption zone 14 and methods ofmaking these sorbents are described in detail in U.S. Pat. Nos.6,429,170 and 7,241,929, the entire disclosures of which areincorporated herein by reference.

Table 1, below, provides the composition of a sorbent employed insorption zone 14 according to an embodiment of the present inventionwhere reduction of the sorbent is carried out prior to introduction ofthe sorbent into sorption zone 14.

TABLE 1 Reduced Sorbent Composition (wt %) Range ZnO M_(A)Zn_(B) PEM_(Z)Zn_((1-Z))Al₂O₄ Broad 10-90  5-80 2-50 2-50 Intermediate 20-6010-60 5-30 5-30 Narrow 30-40 30-40 10-20  10-20 

In an alternative embodiment where the sorbent is not reduced prior tointroduction into sorption zone 14, the promoter metal component cancomprise a substitutional solid metal oxide solution characterized bythe formula M_(X)Zn_(Y)O, wherein M is the promoter metal and X and Yare in the range of from about 0.01 to about 0.99. In one embodiment, Xcan be in the range of from about 0.5 to about 0.9, about 0.6 to about0.8, or 0.65 to 0.75 and Y can be in the range of from about 0.10 toabout 0.5, about 0.2 to about 0.4, or 0.25 to 0.35. In general, X+Y=1.

Table 2, below, provides the composition of an unreduced sorbentemployed in sorption zone 14 according to an embodiment where thesorbent is not reduced prior to introduction into sorption zone 14.

TABLE 2 Unreduced Sorbent Composition (wt %) Range ZnO M_(X)Zn_(Y)O PEM_(Z)Zn_((1-Z))Al₂O₄ Broad 10-90  5-70 2-50 2-50 Intermediate 20-7010-60 5-30 5-30 Narrow 35-45 25-35 10-20  10-20 

As mentioned above, when an unreduced sorbent composition is contactedwith a hydrogen containing compound in sorption zone 14, reduction ofthe sorbent can take place in sorption zone 14. Therefore, when sorbentreduction takes place in sorption zone 14, the initial sorbent contactedwith the raw gas stream in sorption zone 14 can be a mixture of reducedsorbent (Table 1) and unreduced sorbent (Table 2).

In general, the incoming tail gas stream can contact the initial sorbentin sorption zone 14 at a temperature in the range of from about 150° C.to about 1000° C., about 250° C. to about 700° C., or 350° C. to 550° C.and a pressure in the range of from about atmospheric pressure to about5000 psig, about atmospheric pressure to about 1000 psig, or atmosphericpressure to 500 psig. At least a portion of sulfur-containing compounds(and/or other contaminants) in the tail gas stream can be sorbed by thesorbent, thereby creating a sulfur-depleted product gas stream and asulfur-laden sorbent. In one embodiment, sulfur-removal efficiency ofsorption zone 14 can be greater than about 85 percent, greater thanabout 90 percent, greater than about 95 percent, greater than about 98percent, or greater than 99 percent.

As depicted in FIG. 1, at least a portion of the contaminant-depletedproduct gas stream can exit sorption zone 14 via conduit 16. In oneembodiment, the product gas stream can comprise less than about 1 volumepercent, less than about 1000 ppmv, less than about 10 ppmv, or lessthan 1 ppmv of sulfur-containing components. As shown in FIG. 1, thecontaminant-depleted product gas stream can then be routed to a productgas user 16. Product gas user 16 can comprise a vent.

As depicted in FIG. 1, at least a portion of the sulfur-laden sorbentdischarged from sorption zone 14 can be routed to drying zone 18 viaconduit 116. In one embodiment, the sulfur-laden sorbent can have asulfur loading in the range of from about 0.1 to about 27, about 3 toabout 26, about 5 to about 25, or 10 to 20 weight percent. In dryingzone 18, at least a portion of the sulfur-laden sorbent can be dried byflowing an inert gas purge stream in conduit 118 having a temperature inthe range of from about 100 to about 550° C., about 150 to about 500°C., or 200 to 475° C. through the sorbent for a time period of at leastabout 15 minutes, or a time period in the range of from about 30 minutesto about 100 hours, about 45 minutes to about 36 hours, or 1 hour to 12hours. The resulting dried, sulfur-laden sorbent can then be routed toregeneration zone 20 via conduit 120, as illustrated in FIG. 1.

Regeneration zone 20 can employ a regeneration process capable ofremoving least a portion of the sulfur (or other sorbed contaminants)from the sulfur-laden sorbent via contact with a regeneration gas streamunder sorbent regeneration conditions. In one embodiment, theregeneration gas stream entering regeneration zone 20 via conduit 122can comprise an oxygen-containing gas stream, such as, for example, air(e.g., about 21 volume percent oxygen). In another embodiment, theregeneration gas stream in conduit 120 can be an oxygen-enriched gasstream comprising at least about 50, at least about 75, at least about85, or at least 90 volume percent oxygen. In yet another embodiment, theregeneration gas stream can comprise a substantially pure oxygen stream.

According to one embodiment of the present invention, the regenerationprocess employed in regeneration zone 20 can be a step-wise regenerationprocess. In general, a step-wise regeneration process includes adjustingat least one regeneration variable from an initial value to a finalvalue in two or more incremental adjustments (i.e., steps). Examples ofadjustable regeneration variables can include, but are not limited to,temperature, pressure, and regeneration gas flow rate. In oneembodiment, the temperature in regeneration zone 20 can be increased bya total amount that is at least about 75° C., at least about 100° C., orat least 150° C. above an initial temperature, which can be in the rangeof from about 250 to about 650° C., about 300 to about 600° C., or 350to 550° C. In another embodiment, the regeneration gas flow rate can beadjusted so that the standard gas hourly space velocity (SGHSV) of theregeneration gas in contact with the sorbent can increase by a totalamount that is at least about 1,000, at least about 2,500, at leastabout 5,000, or at least 10,000 volumes of gas per volume of sorbent perhour (v/v/h or h⁻¹) above an initial SGHSV value, which can be in therange of from about 100 to about 100,000 h⁻¹, about 1,000 to about80,000 h⁻¹, or 10,000 to 50,000 h⁻¹.

In one embodiment, the size of the incremental adjustments (i.e., theincremental step size) can be in the range of from about 2 to about 50,about 5 to about 40, or 10 to 30 percent of magnitude of the desiredoverall change (i.e., the difference between the final and initialvalues). For example, if an overall temperature change of about 150° C.is desired, the incremental step size can be in the range of from about3 to about 75° C., about 7.5 to about 60° C., or 15 to 45° C. In anotherembodiment, the magnitude of the incremental step size can be in therange of from about 2 to about 50, about 5 to about 40, or 10 to 30percent of magnitude of the initial variable value. For example, if theinitial regeneration temperature is 250° C., the incremental step sizecan be in the range of from about 5 to about 125° C., about 12.5 toabout 100° C., or 25 to 75° C. In general, successive incremental stepscan have the same incremental step sizes, or, alternatively, one or moreincremental step sizes can be greater than or less than the incrementalstep size of the preceding or subsequent steps.

In one embodiment, subsequent adjustments to the regenerationvariable(s) can be carried out at predetermined time intervals. Forexample, adjustments can be made after time intervals in the range offrom about 1 minute to about 45 minutes, about 2 minutes to about 30minutes, or 5 to 20 minutes. In another embodiment, the adjustments canbe made based on the value(s) of one or more “indicator” variable(s). Anindicator variable is a variable in the system monitored to determinethe progress of the sorbent regeneration. Examples of indicatorvariables can include, but are not limited to, sorbent sulfur loading,regeneration sorbent bed temperature, regeneration zone temperatureprofile (i.e., exotherm), and off-gas stream composition. In oneembodiment, the sulfur dioxide (SO₂) concentration in the off-gas streamis monitored to determine when the flow rate of the regeneration gasand/or the regeneration temperature should be incrementally adjusted.

The regeneration process can be carried out in regeneration zone 20until at least one regeneration end point is achieved. In oneembodiment, the regeneration end point can be the achievement of adesired value for one or more of the adjusted regeneration variables.For example, the regeneration process can be carried out until thetemperature achieves a final value in the range of from about 300 toabout 800° C., about 350 to about 750° C., or 400 to 700° C. or theSGHSV reaches a final value in the range of from about 1,100 to about110,000 h⁻¹, about 5,000 to about 85,000 h⁻¹, or 25,000 to 60,000 h⁻¹.In another embodiment, the regeneration process can be finished after apredetermined number of variable adjustments. For example, theregeneration process can be carried out long enough for at least 1 or inthe range of from about 2 to about 8 or 3 to 5 incremental adjustmentsto be made. In yet another embodiment, the regeneration process can becarried out until a final value of the selected indicator variable isachieved. For example, the regeneration process can be carried out untilthe concentration of SO₂ in the off-gas exiting regeneration zone 20declines to a value less than about 1 volume percent, less than about0.5 volume percent, less than about 0.1 volume percent, or less than 500ppmv. Regardless of the specific endpoint selected, the entire length ofthe regeneration process can be less than about 100 hours, or in therange of from about 30 minutes to about 48 hours, about 45 minutes toabout 24 hours, or 1.5 to 12.5 hours.

In one embodiment, the above-described regeneration process can have aregeneration efficiency of at least about 75 percent, at least about 85percent, at least about 90 percent, at least about 95 percent, at leastabout 98 percent, or at least 99 percent. The regenerated sorbent canhave a sulfur loading that is less than about 10 weight percent, or inthe range of from about 0.05 to about 6 weight percent, or 0.1 to 4weight percent.

As illustrated in FIG. 1, at least a portion of the regenerated sorbentin conduit 124 can then be returned to sorption zone 14. As discussedabove, in one embodiment, at least a portion of the regenerated sorbentdoes not undergo a reduction step prior to introduction into sorptionzone. In such an embodiment, the regenerated but unreduced sorbentintroduced into sorption zone 14 can comprise an unreduced promotermetal component that includes a substitutional solid metal oxidesolution characterized by the formula M_(X)Zn_(Y)O (See e.g., Table 3,above).

Referring back to FIG. 1, the off-gas stream exiting regeneration zone20 via conduit 126 can subsequently be routed to off-gas user 22.Off-gas user 22 can comprise any unit capable of processing the off-gasstream, such as, for example, a Claus sulfur processing unit. In oneembodiment, the off-gas stream exiting regeneration zone 20 via conduit126 can comprise at least about 5, at least about 10, at least about 20,or at least 25 volume percent SO₂. In one embodiment, the off-gas streamcomprises less H₂S than in the tail gas stream entering sorption zone 14via conduit 112. In another embodiment, off-gas stream can comprisesubstantially no H₂S.

EXAMPLES

The following examples are intended to be illustrative of the presentinvention and to teach one of ordinary skill in the art to make and usethe invention. These examples are not intended to limit the invention inany way.

A sorbent was exposed to several simulated feeds representing varioustail gas compositions. The feeds had a general H₂S to SO₂ ratio of about2:1.

Sorbents containing nickel, zinc, alumina, and expanded perlite werecrushed and sieved to obtain 100+/200− mesh size particles. The sorbentswere then contacted with the simulated tail gas streams. For Example 2,the sorbent was reduced with hydrogen before being contacted with thefeeds, and for Examples 3-5, the sorbents were reduced in-situ duringcontact with the feeds.

A 1:1 mixture of sorbent and alundum was used to prevent the reactor bedfrom plugging. This mixture was placed in a downflow fixed bed reactorand heated to 400° C. and slightly elevated pressure to warrant feedflow through the system. To prevent steam from condensing in thereactor, all sample lines, valves, and other sample system componentswere heat-traced to maintain a temperature above 150° C. both up-anddownstream of the reactor. Before analyzing the downstream off-gases,the steam was condensed to protect the on-line analyzers. For Examples3-5, where a pre-reduction step was carried out, the sorbent was exposedto a 20 volume percent H₂/N₂ gas mixture until water levels in theoff-gas were back to approximately their initial levels.

Example 1

This Example was conducted using an unreduced sorbent. The feed streamused contained N₂ with 243 ppmv SO₂ and 243 ppmv H₂S. FIG. 2 shows thatH₂S is sorbed, but SO₂ remains in the off-gases.

Example 2

In this Example, the sorbent was pre-reduced with H₂. In this case,complete conversion and storage of both contaminants into the sorbentwas achieved. This reaction continued as long as reduced activecomponents were available. Even when these resources neared exhaustion(after 50+ minutes), H₂S was still removed due to the excessavailability of ZnO. This is shown in detail in FIG. 3.

Example 3

In this Example, a small amount of a reductant (H₂) was added to thefeed. This in-situ reduction forms active species capable of reducingSO₂ and storing the resulting sulfur into the sorbent. This is shown inFIG. 4. When the source of H₂ was removed, simultaneous removal of H₂Sand SO₂ continued for approximately 8000 seconds, after which the amountof SO₂ in the feed or effluent increased.

Example 4

A gas composition resembling refinery off-gases was simulated to showthat both SO₂ and H₂S can be removed under these conditions. These gasestend to contain larger amounts of steam. The gas composition studied isshown in Table 3.

TABLE 3 Refinery Gas Simulation Component Amount SO₂ [ppm] 2000 H₂S[ppm] 10000 H₂ [%] 1 CO [%] — CO₂ [%] 4 H₂O [%] 32 Balance N₂The results are shown in FIG. 5. The sorbent achieved comparable removallevels to detection limits for both contaminants as long as reducedactive components (Ni and Zn) were available.

Example 5

A Claus unit tail gas simulation was also tested. This tail gas containssyngas, CO₂, H₂S and SO₂, but very low moisture levels. Table 4 belowshows the composition of the Claus unit tail gas tested.

TABLE 4 Claus Simulation Component Amount SO₂ [ppm] 330 H₂S [ppm] 660 H₂[%] 20 CO [%] 20 CO₂ [%] 8 H₂O [%] — Balance N₂FIG. 6 shows that the sorbent achieved the same removal efficiencyobserved before for other feed compositions.

1. A process for the simultaneous removal of SO₂ and H₂S, said process comprising; a) contacting a tail gas stream comprising of SO₂ and H₂S with a sorbent in a sorption zone to produce a product gas stream and a sulfur laden sorbent, wherein said sorbent comprises Zn and a promoter metal; and b) contacting at least a portion of said sulfur laden sorbent with a regeneration gas stream in a regeneration zone to produce a regenerated sorbent and an off-gas stream.
 2. A process in accordance with claim 1 wherein said promoter metal is nickel.
 3. A process in accordance with claim 1, wherein said sorbent comprises a substitutional solid metal solution characterized by the formula M_(A)Zn_(B), wherein M is said promoter metal, wherein A and B are in the range of from about 0.01 to about 0.99.
 4. A process in accordance with claim 1, further comprising, prior to step (b), drying at least a portion of said sulfur-laden sorbent to thereby provide a dried sulfur-laden sorbent and subjecting at least a portion of said dried sulfur-laden sorbent to said contacting of step (b).
 5. A process in accordance with claim 1, further comprising introducing at least a portion of said regenerated sorbent into said sorption zone, wherein said regenerated sorbent introduced into said sorption zone comprises a substitutional solid metal oxide solution characterized by the formula M_(X)Zn_(Y)O, wherein M is said promoter metal, wherein X and Y are in the range of from about 0.01 to about 0.99.
 6. A process in accordance with claim 1, wherein said tail gas stream comprises SO₂ in the range of up to about 5 volume percent, based on the total volume of said tail gas stream.
 7. A process in accordance with claim 1, wherein said tail gas stream comprises H₂S in the range of up to about 5 volume percent, based on the total volume of said tail gas stream.
 8. A process in accordance with claim 1, wherein said tail gas stream has a ratio of H₂S to SO₂ of about 100:1.
 9. A process in accordance with claim 1, wherein said tail gas stream has a ratio of H₂S to SO₂ of about 10:1.
 10. A process in accordance with claim 1, wherein said tail gas stream has a ratio of H₂S to SO₂ of about 2:1.
 11. A process in accordance with claim 1 wherein said tail gas stream further comprises compounds selected from the group consisting of steam, syngas, CO₂, and combinations of any two or more thereof.
 12. A process in accordance with claim 1 wherein said sorbent is reduced with a reducing agent in a reduction zone prior to said contacting of said tail gas stream in step (a).
 13. A process in accordance with claim 12 wherein said reducing agent comprises an agent selected from the group consisting of hydrogen and carbon monoxide.
 14. A process in accordance with claim 1 wherein said tail gas further comprises a reducing agent.
 15. A process in accordance with claim 14 wherein said reducing agent comprises an agent selected from the group consisting of hydrogen and carbon monoxide.
 16. A process in accordance with claim 1 wherein conditions in said sorption zone include a temperature in the range of from about 150° C. to about 1000° C.
 17. A process in accordance with claim 1 wherein conditions in said sorption zone include a temperature in the range of from about 250° C. to about 700° C.
 18. A process in accordance with claim 1 wherein conditions in said sorption zone include a temperature in the range of from about 350° C. to about 550° C.
 19. A process in accordance with claim 1 wherein conditions in said sorption zone include a pressure in the range of from about atmospheric pressure to about 5000 psig.
 20. A process in accordance with claim 1 wherein conditions in said sorption zone include a pressure in the range of from about atmospheric pressure to about 1000 psig.
 21. A process in accordance with claim 1 wherein conditions in said regeneration zone includes a regeneration gas stream.
 22. A process in accordance with claim 21 wherein said regeneration gas stream comprises oxygen.
 23. A process in accordance with claim 21 wherein said regeneration gas stream comprises air.
 24. A process in accordance with claim 1 wherein said off-gas stream comprises SO₂.
 25. A process in accordance with claim 24 wherein said offgas stream is recycled to a SO₂ treatment zone.
 26. A process in accordance with claim 25 wherein said SO₂ treatment zone comprises a Claus unit.
 27. A process in accordance with claim 1 wherein at least a portion of said regenerated sorbent is returned to said sorption zone.
 28. A process for the simultaneous removal of SO₂ and H₂S, said process comprising: a) reducing a sorbent with a reducing agent in a reduction zone to form a reduced sorbent, wherein said reduced sorbent comprises Zn, expanded perlite, and a promoter metal, wherein at least a portion of said reduced sorbent comprises a substitutional solid solution characterized by the formula M_(Z)Zn_((1-Z))Al₂O₄ and a substitutional solid metal solution characterized by the formula M_(A)Zn_(B), wherein M is a promoter metal component and A, B, and Z are in the range of from about 0.01 to about 0.99; b) contacting said reduced sorbent with a tail gas stream comprising SO₂ and H₂S in a sorption zone to produce a product gas stream and a sulfur laden sorbent; c) regenerating said sulfur laden sorbent in a regeneration zone to produce a regenerated sorbent and an off gas comprising SO₂; d) returning at least a portion of said regenerated sorbent to said sorption zone; and e) recycling said SO₂ containing off gas to a SO₂ treatment zone.
 29. A process in accordance with claim 28 wherein said SO₂ treatment zone comprises a Claus unit.
 30. A process in accordance with claim 28 wherein conditions in said sorption zone include a temperature in the range of from about 150° C. to about 1000° C.
 31. A process in accordance with claim 28 wherein conditions in said sorption zone include a temperature in the range of from about 250° C. to about 700° C.
 32. A process in accordance with claim 28 wherein conditions in said sorption zone include a temperature in the range of from about 350° C. to about 550° C.
 33. A process in accordance with claim 28 wherein conditions in said sorption zone include a pressure in the range of from about atmospheric pressure to about 5000 psig.
 34. A process in accordance with claim 28 wherein conditions in said sorption zone include a pressure in the range of from about atmospheric pressure to about 1000 psig.
 35. A process in accordance with claim 28 wherein conditions in said regeneration zone includes a regeneration gas stream.
 36. A process in accordance with claim 28 wherein said regeneration gas stream comprises oxygen.
 37. A process in accordance with claim 28 wherein said regeneration gas stream comprises air.
 38. A process in accordance with claim 28 wherein said reduction zone of step (a) and said sorption zone of step (b) are in the same vessel.
 39. A process in accordance with claim 28, wherein said tail gas stream comprises SO₂ in the range of up to about 5 volume percent, based on the total volume of said tail gas stream.
 40. A process in accordance with claim 28, wherein said tail gas stream comprises H₂S in the range of up to about 5 volume percent, based on the total volume of said tail gas stream.
 41. A process in accordance with claim 28, wherein said tail gas stream has a ratio of H₂S to SO₂ of about 2:1.
 42. A process in accordance with claim 28 wherein said tail gas stream further comprises compounds selected from the group consisting of steam, syngas, CO₂, and combinations of any two or more thereof.
 43. A process in accordance with claim 28 wherein said reducing agent comprises an agent selected from the group consisting of hydrogen and carbon monoxide. 